Brandon asksCan you help me understand all of these Damascus steel knives I keep seeing?  They look gorgeous, but are they just for looks?  Would one of these make for a good all-around knife?

Well, that’s a complicated question. First, let’s do a little freshening up on what exactly “Damascus steel” is. Damascus, Wootz, and patternweld are all names given to different types of steels and blades. Basically, the idea is that two or more steel alloys are forged/cast together through various methods to give the wavy artistic pattern that comes from such a layering process. Unfortunately, the technique for making both Damascus and Wootz steel has been lost to the centuries. Anyone claiming to be making authentic Wootz/Damascus these days is delusional. Or lying . . .

wootz dagger

wootz steel dagger

Traditional dagger cut from wootz ingot

99.9999% of the layered and forged steel these days is either san-mai or pattern welded (mokume and mosaic are a different thing all together.) San-mai steel is very common in Japanese knives, and it’s literally just a sandwich of 3 sheets of steel. Two outer stainless steels and a harder stainless or carbon steel core make up the cross section of a San-mai blade. No folding is done on a San-mai blade because the goal is to have a hard, protected edge that’s fused to the stainless steel but not mixed with it.

The other type of pattern-welded steel is the so called “Damascus steel”. Originally used in middle eastern sword making, the method has been lost since about the 16th century. The art form has resurfaced, though, and in 1973 bladesmith William F. Moran unveiled his “Damascus knives” at the Knifemakers’ Guild Show. Ever since then modern pattern-welded steel blades have been called “Damascus knives”.

You asked what they are used for. Well…the process of choosing steel for a Damascus blade is important. Many makers choose 2-5 alloys that play nicely together and make for a beautiful pattern. Once the knife is forged or ground to shape, the waves of steel alloy will meet at the edge and you can change the cutting performance of the blade by tweaking the alloy and its heat treat process.

devin Damascus steel blade

Zig-zag Damascus steel

210mm gyuto stainless damascus with 19c27 core, wenge handle

For instance Devin Thomas is a master Damascus steel maker. He forges every billet himself and has the process down to a science. Devin makes all-stainless Damascus steel, high contrast, double high carbon, and many, many exotic patterns. When he uses AEB-L and 304 together, it’s obvious that some of the stronger qualities of AEB-L will be watered down by the softer 304. But remember — forged together in a blade, differing alloys present at the blade’s edge can make for a micro-serration surface, aiding in sawing or slicing actions.

When it comes down to it, most of today’s super exotic alloys will outperform any pattern-welded steel. Owning and using a Damascus steel blade is about personal style and respect for the time and process of developing such a blade. A well-made Damascus blade will stay sharp for longer than most production quality knives, but if you’re looking for the ends-of-the-earth best performing blade steel, look elsewhere.

As with any knife-related subject, quality is largely determined by how much it costs. True “name brand” Damascus steel is of the highest quality. Devin Thomas, Chad Nichols, Brad Vice, and Rob Thomas are all makers that forge each billet with quality and care. Knives made from these steels will make fantastic knives. Unfortunately cheap knockoff stuff from China, Pakistan and India shows up on Ebay and other online retailers all the time. These knives are junk and will disappoint you. The rule of thumb is, if the price is too good to be true, it is.

If you have more questions on the subject, I’ll be more than happy to answer you in the comments.

For a great video explanation of Damascus steel from Knifemaker, click below. it is a great compliment to this article 

Knifemaker Will Woods is owner of Woods Bladeworks. He is TTAK’s “Knifemaker in Residence” and contributing author.